Synthesis of fluorine-graphite intercalation compounds by elemental fluorine and high oxidation-state transition-metal fluorides

Fluorine-graphite intercalation compounds have been synthesized using high purity fluorine gas and high oxidation-state transition-metal fluorides, AgF₃ and NiF₃, at room temperature and at −78 °C. At room temperature, a mixture of stage 1 + 2 − 4 compounds with compositions, C_4.2F to C_14.6F were obtained. On the other hand, stage 2–4 compounds with compositions C_5.6F to C_14.2F were synthesized at −78 °C. The fluorinating ability of AgF₃ and NiF₃ has been shown more clearly at room temperature because a small amount of fluorine was intercalated/absorbed into graphite at −78 °C without catalysts. XPS spectra show that ionic, nearly ionic, semi-covalent and covalent fluorines coexist in the C_xF samples, and that the covalency of CF bonding increases with decreasing stage number.     

Continuous hydrogenation of vegetable oils in reactors equipped with static mixers

Continuous hydrogenation of industrially refined soybean oil with Harshaw Ni catalyst was achieved in a slurry column equipped with Sulzer SMV motionless mixers. The influence of the operating parameters (temperature, pressure, catalyst concentration and gas velocity) was investigated. The presumption that, in this equipment, the liquid-solid mass transfer limits the rate of the process is in good agreement with the experimental data.     

纳米级氢氧化镍制备及电化学性能研究

介绍了一种通过合成草酸镍,进而生成β型纳米氢氧化镍的新的合成路线,从而达到大幅度提高镍氢电池正极放电容量的目的。使用X射线衍射（XRD）分析产品的晶型结构。从产品谱图中可以得知：由于特征衍射峰的出现可以判定该产品为β型,且由于（001）峰的宽化可以初步判定其为纳米级。通过透射电镜（TEM）可以看出产品粒径和形貌的具体特征,即产品为针状,长度为100～200 nm,直径为10～20 nm。将纳米级氢氧化镍制成电极,经过充放电测试可以发现电容量约为400 mA.h/g,远远高于球形微米级氢氧化镍的放电容量。     

废镍触媒的综合利用

本文采用酸溶，除渣，分离及蒸发浓缩，冷却，过滤等操作步骤，从废镍触媒中回收得有实用价值的硫酸镍，硫酸镁晶体，其回收率分别为７５％和９０％，经济效益也比较好。     

Suppression of the α → β-nickel hydroxide transformation in concentrated alkali: Role of dissolved cations

The presence of dissolved cations such as Al and Zn in alkaline electrolyte (6 M KOH) suppresses the -nickel hydroxide transformation. The uptake of Al (10 mol%) and Zn (30 mol%) exhibited by the active material likely stabilizes the -phase. Dissolved Al is deleterious to the performance of the nickel hydroxide electrode, whereas, dissolved Zn enhances the specific discharge capacity of nickel hydroxide by approximately 25% showing that the mode of metal uptake is different in the two cases.     

Activity–Composition Relations in NiAl2O4─MnAl2O4 Solid Solutions and Stabilities of NiAl2O4 and MnAl2O4 at 1300° and 1400°C

Activities of NiO were measured in the oxide and spinel solutions of the system MnO–NiO–Al₂O₃ at 1300° and 1400° C with the aim of deriving information on the thermodynamic properties of the spinel phases. Synthetic samples in selected phase assemblages of the system were equilibrated with metallic nickel and a gas phase of known oxygen partial pressures at a total pressure of 1 atm. The data on NiO activities and directions of conjugation lines between coexisting oxide and spinel phases were used to establish the activity–composition relations in spinel solid solutions at 1300° and 1400°C. The MnAl₂O₄–NiAl₂O₄ solid solutions exhibit considerable negative deviations from ideality at these temperatures. The free energy of formation of MnAl₂O₄ from its oxide components (MnO + Al₂O₃) at 1300° and 1400°C is calculated to be −24.97 and −26.56 kJ. mol⁻¹, respectively. The activities determined in the stoichiometric spinel solid solutions are more negative as compared with those predicted from cation distribution models.     

负载型复合载体对Ni基催化剂催化性能的影响

将ZrO2直接负载在MxOy（Al2O3,SiO2,CeO2）上组成负载型ZrO2/MxOy复合载体,并以此负载型复合载体制备Ni基催化剂,用BET、XRD、TPR和TPD等对催化剂的比表面积、晶相结构、还原性能等进行了表征,同时以CO2重整CH4为探针考察了催化剂的活性和稳定性。结果表明,复合载体对Ni基催化剂的性能有较大的影响：Ni/ZrO2/SiO2具有较好的初活性,但反应5 h后明显下降;Ni/ZrO2/Al2O3在反应50 h后CO2和CH4的转化率基本保持不变。     

纳米氧化镍纤维的制备及表征

利用静电纺丝法,制备出聚乙烯吡咯烷酮(PVP)/四水乙酸镍纤维前躯体,通过焙烧前躯体制备出纳米氧化镍纤维,并用透射电子显微镜(TEM),扫描电子显微镜(SEM),X-射线衍射(XRD)以及热重分析(TG)对纤维进行了表征.     

Electroless nickel plating on the surface of carbon fibers

The electroless nickel plating on the surface of carbon fibers was prepared by pretreating the carbon fibers in order to increase their conductivity,and consequently enhance the EMI shielding effectiveness of the composites.The relationship between the performance of depositing coat and pH value,temperature,reaction time and the way of agitation was studied.Results show that the depositing quality is stable under pH between 4.5 and 5.0,temperature between 75 ℃ and 85 ℃,reaction time for 10 min and air agitation.The uniform and compact nickel layer deposited on carbon fibers was proved by XRD and SEM,and the electrical resistivity of carbon fibers with nickel coating was tested.Results indicate that the electrical resistivity of carbon fibers with electroless nickel plating is decreased by an order of magnitude compared with that of carbon fibers.It means that nickel coating can greatly improve the electromagnetic interference shielding properties of carbon fibers.     

复合掺杂Nd（III）和Zn（II）非晶态Ni（OH）2电极活性材料的制备及其表征

以NiSO4、ZnSO4和Nd（NO3）3为原料,采用共沉淀快速冷冻法制备出了复合掺杂稀土Nd（III）和Zn（II）的非晶态氢氧化镍粉体材料。测试发现：样品材料微结构无序性强,结晶水含量较高。将样品材料制备成镍电极并组装成MH—Ni电池,在80mA／g恒电流充电5．5h、40mA／g恒电流放电、终止电压为1．0V的充放电制度下,复合掺杂6％Nd（III）和6％Zn（II）样品材料电池的放电平台为1．2624V,放电比容量为343．12mAh／g,远高于目前应用的B-Ni（OH）2电极活性材料的放电比容量。